Polyurethane Iron Red Kun

Polyurethane iron pupa alakoko, polyurethane iron pupa egboogi-ibajẹ alakoko, polyurethane iron pupa egboogi-ibajẹ.

Red polyurethane alakoko (Pupa polyurethane alakoko) oriširiši hydroxyl-ti o ni resini, iron oxide pupa, antirust pigmented kikun, additives, epo, ati be be lo, ati ki o kan meji-paati polyurethane iron pupa kun kq ti polyisocyanate prepolymer.

Constructability: Ko si idiwọ si ohun elo
Irisi fiimu: deede
Ipo ninu eiyan: ko si awọn lumps lile lẹhin igbiyanju ati dapọ, ni ipo iṣọkan.
Akoko gbigbe: gbigbe dada ≤ 1h, gbigbẹ to lagbara ≤ 24h (itọka boṣewa: GB/T1728-79)
Idaabobo omi iyọ: ko si fifọ, ko si roro, ko si itasilẹ ( atọka boṣewa: GB/T9274-88)
Idaabobo acid: ko si sisan, ko si roro, ko si peeling (Atọka boṣewa: GB/T9274-88)
Idaabobo alkali: ko si sisan, ko si roro, ko si peeling (atọka boṣewa: GB/T9274-88)
Idaabobo atunse: 1mm (Atọka boṣewa: GB/T1731-1993)
Idaabobo ikolu: 50cm (itọka boṣewa: GB/T4893.9-1992)
Pre-coating: Taara ya lori irin dada ti descaling didara Gigun Sa2.5 ite.
Lẹhin ti o baamu: polyurethane mica paint, polyurethane paint, acrylic polyurethane top coat, fluorocarbon top ndan.

Niyanju film sisanra: 60-80um
Nọmba ti a ṣe iṣeduro ti awọn ẹwu: 2 ~ 3 aso
Ibi ipamọ otutu: -10 ~ 40°C
Iwọn otutu ikole: 5 ~ 40°C
Akoko idanwo: 6h
Ọna ikole: Brushing, air spraying, sẹsẹ le ṣee lo.
Iwọn lilo imọ-jinlẹ: nipa 115g/m² (da lori fiimu gbigbẹ 35um, laisi pipadanu)
Aarin kikun: otutu otutu ℃ 5-10 15-20 25-30 Kukuru aarin h 48 24 12 Aarin gigun ko ju ọjọ meje lọ.
Iwọn otutu sobusitireti gbọdọ ga ju aaye ìri ti o ju 3 ℃, nigbati iwọn otutu sobusitireti ba kere ju 5 ℃, fiimu kikun ko ni arowoto, ko dara fun ikole.

O dara fun eto irin, ojò epo, ojò epo, ohun elo anticorrosion kemikali, ohun elo elekitiroki, awọn ọkọ irinna bi ibora priming antirust.

Lẹhin ṣiṣi agba ti paati A, o gbọdọ rú daradara, ati lẹhinna tú ẹgbẹ B sinu paati A labẹ aruwo ni ibamu si awọn ibeere ti ipin, dapọ daradara, fi silẹ, jẹun fun 30min, ṣafikun iye to yẹ ti diluent ati ṣatunṣe o si iki ikole.
Diluent: diluent pataki fun jara polyurethane.
Sokiri laisi afẹfẹ: iye fomipo jẹ 0-5% (nipa ipin iwuwo ti kikun), alaja nozzle jẹ 0.4mm-0.5mm, titẹ fifa jẹ 20MPa-25MPa (200kg/cm²-250kg/cm²).
Afẹfẹ spraying: Dilution iye jẹ 10-15% (nipa àdánù ipin ti kun), nozzle caliber jẹ 1.5mm-2.0mm, spraying titẹ jẹ 0.3MPa-0.4MPa (3kg/cm²-4kg/cm²).
Rola ti a bo: Iye fomipo jẹ 5-10% (nipasẹ iwọn iwuwo kikun)

Ni awọn ga otutu akoko ikole, rọrun lati gbẹ sokiri, ni ibere lati yago fun gbẹ sokiri le ti wa ni titunse pẹlu tinrin titi ko gbẹ sokiri.
Ọja yii yẹ ki o lo nipasẹ awọn oniṣẹ kikun ọjọgbọn ni ibamu si awọn itọnisọna lori package ọja tabi afọwọṣe yii.
Gbogbo iṣẹ ti o kan ohun elo ati lilo ọja yii gbọdọ ṣee ṣe ni ibamu pẹlu gbogbo ilera ti o yẹ, ailewu ati awọn ilana ayika ati awọn iṣedede.
Ti o ba ni iyemeji boya o yẹ ki o lo ọja yii, jọwọ kan si Ẹka Iṣẹ Imọ-ẹrọ wa fun awọn alaye.

Awọn ọja yẹ ki o wa ni ipamọ ni ibi ti o tutu ati ti afẹfẹ, idilọwọ imọlẹ orun taara, ati sọtọ lati awọn orisun ti ina, kuro lati awọn orisun ooru ni ile-itaja.
Nigbati o ba n gbe ọja naa, o yẹ ki o ni aabo lati ojo ati oorun, yago fun ikọlu, ati ni ibamu si awọn ilana ti o yẹ ti ẹka ijabọ.

Aaye ikole yẹ ki o ni awọn ohun elo afẹfẹ ti o dara, ati awọn oluyaworan yẹ ki o wọ awọn gilaasi, awọn ibọwọ, awọn iboju iparada, ati bẹbẹ lọ lati yago fun ifarakan ara ati ifasimu ti owusu awọ.
Siga ati ina ti wa ni idinamọ muna ni aaye ikole.